Hot Melt Glue Transparent Sheets Hot Melt Film Backing for Chenille Embroidery Patch
Description:
Hot melt Glue Transparent Sheets is us through the high precision coating machine to coating the melting raw materials well-distributed into the release paper, and the thin film colors is transparent.It is usually used to bonding apperals and Chenille embroidery patch industies. But It is also widely usd to bonding cottons, leathers, woods, papers, aluminum and other metarils. At the same time, it is also have good washable and resist chemical additives.
Physical Characteristics:
| Color | Transparent | Release Liner | Glassine release paper |
| Density | 1.2±0.02g/cm³ | Conventional thickness | 0.1mm,0.12mm,0.15mm,0.18mm |
| Melt Flow Index | 32±5g/10min ASTMD1238-04 | Conventional Width | 48cm,50cm,96cm,100cm,150cm |
| operating Temperature | 120℃-160℃ | Length | 100yards/100meters or it's up on your option. |
| Flow Beginning Point | 108℃±5℃ | Reguler Specification | 48cm (width)*100yards(Length) /roll |
| Recommended Bonding Conditions | |||
| First Lamination | Second Implanting | ||
| Mechanical Mold Temperature | 120℃-130℃ | Mechanical Mold Temperature | 140℃-170℃ |
| Hot Pressing Time | 3-5 seconds | Hot Pressing Time | 8-15 seconds |
| Pressure | 0.3-0.6mpa | Pressure | 0.3-0.6mpa |
Others Suggestions:
| Hot Melt Adhesive Film For Chenille Embroidery Patch | ||
| Type | HT03 | HT07-60L |
| Color | Milky White | Transparent |
| Bottom Materials | Silicon Glassine Release Paper | |
| Melt Point(℃) | 108 | 100 |
| Pressing Temperature(℃) | 120-160 | 130-160 |
| Adhesive Strengh(N/1c㎡) | >80 | >80 |
| Normal Thickness | 0.06mm,0.08mm,0.1mm, 0.12mm,0.15mm,0.18mm | |
| Normal Specification (width*length) | 50cm*100YDS | 50cm*100YDS |
| Washable | ||
| 40(℃) | *** | *** |
| 60(℃) | ** | ** |
| 80(℃) | * | * |